Electroless nickel deposition (ELD) on polymer substrates enables the fabrication of flexible, conductive fibres for wearable and functional textiles. However, achieving uniform, low-defect coatings on synthetic fibres such as nylon-6,6 remains challenging due to their chemical inertness, hydrophobicity, and poor interfacial compatibility with metal coatings. This study presents a solvent-assisted approach using dimethyl sulfoxide (DMSO) in a conventional aqueous ELD bath to control both polymer-metal interfacial chemistry and nickel coating microstructure. The modified surface supports dense catalytic sites, triggering spatially uniform Ni nucleation. The combination of scanning electron microscopy and transmission electron microscopy confirms the difference in coarse grains with fully aqueous baths to a nanocrystalline shell with DMSO-modified baths. This refined microstructure relieves residual stress and anchors firmly to the swollen polymer, delivering +7 °C higher onset decomposition temperature and 45% lower creep strain at 50 °C compared with aqueous controls. The fabric strain sensor fabricated by 1 wt.% DMSO-modified ELD shows a remarkable sensitivity against strain, demonstrating a 1400% resistance change under 200% stain. Electrochemical impedance and polarisation tests confirm a two-fold rise in charge transfer resistance and negligible corrosion current drift after accelerated ageing. By clarifying how a polar aprotic co-solvent couples polymer swelling with metal growth kinetics, the study introduces a scalable strategy for tuning polymer-metal interfaces and advances solvent-assisted ELD as a route to mechanically robust, thermally stable, and corrosion-resistant conductive textiles.
Keywords: conductive functional textile; nanocrystalline coatings; polymerisation treatment; solvent-assisted electroless deposition; surface activation; thermal stability.